alumina crackles can't be used on the Growth of sapphire Single Crystal

Word:[Big][Middle][Small] QR Code 2018-10-16     Viewed:    

Alumina crystalline block can't be used on the Growth of Single Crystal

development plan of LED industry》  2012/ 01/ 12   deng yu zhi

    Presently,many companies use alumina crystalline block -a kind of transparent crystal to grow single 

crystalline in China.Resultantly,the sapphire ingots contain more impurities,own more bubbles and 

more dislocations,and can't be used on LED field.Why?

  The crystalline block is produced with flame fusion method.The disadvantage of the method is as follows:

     First, screen the alumina powder from the roof through vibration screen,the screened powder will cool and 

consolidate on the core crystalline during falling after through oxyhydrogen flame with high temperature(the crystalline

 granules is half transparent,and more Taiwan customers are crazy with it,who think themselves its purity is relatively

 high and transparent.But,in fact,the purity is only 99.9% -99.97% according to test. )These impurities such as Fe,Si,Ti 

will directly affect the transparency of Sapphire ingots.And they will depend usage rate in LED field at last. According

 to test,content of Fe is 79 ppm,K is 800ppm.And when content of CaMg is more,the sapphire ingots easily break.

         Second,Hydrogen goes to the furnace body through stainless steel tube which will bring some impurities such as Fe,

Ni,Cr,Ti and other metal impurities along ,which will be a part of sapphire.As melting temperature of alumina is 2050°,

while that of Fe,Ti,CrMg is 2200°and evaporating temperature is over 4000°.And oxyhydrogen flame can only blow

 less light impurities on the surface,having no effect on the inside impurities.

        Third,according to the test report by authoritative experts,170 cubic hydrogen is needed to produce 1KG alumina 

crystalline granules,which will cost RMB150-230.In order to make profits,factories have to use low purity alumina 

(99.9% or 99.99%)instead of high purity ones.However,the transparent surface of such crystalline granules has cheated

 many people.

    Fourth,in the production process of alumina powder,when the calcination temperature is too low, Ammonium Aluminum 

Sulfate can't be decomposed completely,the alumina powder will contains more aluminum sulfate.In the sapphire growing 

process, aluminum sulfate will be decomposed again,which will produce more bubbles in the ingots.

        Fifth,sapphire ingots growed by alumina crystalline block are colorful in that the block contains more impurities.To cover

 fault color,factories usually mix some metal ions.These ions don't display color in the oxidizing atmosphere,but display color 

in the deoxidizing atmosphere.While production method of sapphire ingots are HEN,Cz,Kyropoulos,Bridgman Method with

 the deoxidizing atmosphere.

         From the above,we can see alumina crystalline block can't be used to grow sapphire ingots due to its limits.

         Now only Hydrolysis of Aluminum Alkoxide method can produce real high purity alumina (99.999%-99.9999%)home and abroad.In China ,only xuan cheng jing rui new material co.,ltd adopts the method.In the future,if you want to

capture LED market,you must choose the real high purity alumina.